ASM Material Data Sheet -
Find the modulus of elasticity, tensile strength, yield strength, and other properties of aluminum 6061-T6 and T651 alloys. The modulus of elasticity is 68.9 GPa or 10000 ksi
We are more than an aluminium alloy solution provider.
Do you need consumer aluminium alloy products or learn more info about aluminum alloy prices?
Find the modulus of elasticity, tensile strength, yield strength, and other properties of aluminum 6061-T6 and T651 alloys. The modulus of elasticity is 68.9 GPa or 10000 ksi
Aluminum 6061-T6; 6061-T651. General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength,
Brief introduction to 6xxx wrought aluminum alloys. Tabular data of yield strength, tensile strength, elongation, and modulus of elasticity, at elevated temperatures and at room
Find the modulus of elasticity and other physical, mechanical, electrical and thermal properties of aluminum 6061-T6, a common type of aluminum metal. Learn about its
General 6061 characteristics and uses: Notes: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high. strength, good workability,
6061-T6 aluminum is 6061 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard
6061 Aluminum is a precipitation-hardened aluminum alloy containing magnesium and silicon as its major alloying elements. It is one of the most versatile of the heat-treatable
Property 6061-T4 6061-T6 Tensile Strength 241 MPa | 35000 psi 310 MPa | 45000 psi Yield Strength 145 MPa | 21000 psi 276 MPa | 40000 psi Modulus of Elasticity 68.9 GPa |
Applications: Aircraft fittings, camera lens mounts, couplings, marines fittings and hardware, electrical fittings and connectors, decorative or misc. hardware, hinge pins, magneto
6061-T6 aluminum is 6061 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. Elastic (Young\'s, Tensile) Modulus. 69 GPa 10 x psi. Elongation at Break. 10 % Fatigue Strength. 96 MPa 14 x psi. Poisson\'s Ratio. 0.33
Modulus of Elasticity 69.0 GPa 10000 ksi Poissons Ratio 0..33 Fatigue Strength 100 MPa 14500 psi Mability ALUMINUM COMMON GRADE 6061 WITH T6 Aluminum Alloy Common Grade 6061 w/T4 TemperTEMPER Alliance LLC 1150 Eastport Center Dr. Valparaiso, IN. 46383 :
UNS A96061; ISO AlMg1SiCu; Aluminium 6061-T651, AD-33 (Russia); AA6061-T651 Physical Properties Metric English Comments Density 2.70 g/cc 0.0975 lb/in³ AA; Typical Mechanical Modulus of Elasticity 68.9 GPa 10000 ksi AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than modulus. Notched
Modulus of elasticity and Poisson\'s coefficient of non-ferrous metals. - 6061: aluminum of naval use, also used in pipes and in ultrasonic transducers for cleaning. - 7075: aircraft structures, applications subjected to high voltages and ultrasonic transducers for welding. It is usually available in plates or square
Aluminum alloy 6061 Al Mg1SiCu • Density: 2.7 • Modulus of elasticity in N/mm2: - at 20°C: 68.9 x
Modulus of Elasticity (ksi x 1000) 10.0 10.0 * 6061-T6 / 6061-T651 data shown for comparison to 6061-T4. PRODUCT DETAILS 6061-T4 ALUMINUM SHEET AED Motorsport Products Ltd aedmotorsport 5373 W. th St. Indianapolis, IN 46268 USA Ph. 317.334.0569
The modulus of elasticity for A992 steel is 200 GPa, and for 6061-T6 aluminum alloy is 68.9GPa. The coefficient of thermal expansion for A992 steel is 12 The assembly shown consists of two A992 steel bolts A B and E F and an 6061-T6 aluminum rod C D
Aluminum 6061-O. Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Modulus of Elasticity: 68.9 GPa: 10000 ksi AA; Typical; Average of tension and compression. 0-100 Scale of Aluminum Alloys: Shear Modulus: 26 GPa: 3770 ksi Estimated from similar Al alloys. Shear Strength: 82.7 MPa: 12000
Modulus of Elasticity: 73.1 GPa: 10600 ksi AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. 0-100 Scale of Aluminum Alloys: Shear Modulus: 28 GPa: 4060 ksi : Shear Strength: 290 MPa: 42000 psi AA; Typical: Electrical Properties: Electrical Resistivity: 4.32e-006
6061 Aluminum is a precipitation-hardened aluminum alloy containing magnesium and silicon as its major Modulus of Elasticity, ksi 10000 Ultimate Tensile Strength, ksi .2% Yield Strength, ksi 40 Elongation, % 17 Rockwell Hardness B (Rb) 60 Temperature, F-300 -100 - 500
Aluminum 6061 is one of the most common alloys of aluminum for general-purpose use. 6061 is a precipitation-hardened aluminum alloy, containing magnesium and silicon as its major alloying elements. It has good mechanical properties, exhibits good weldability, and is very commonly extruded. Modulus of Elasticity : 68.9:
Modulus of Elasticity Torsion: 3.8 6061 Aluminum is, by most any measure, the most commonly used aluminum alloy. It is specified in most any application due to its strength, heat treatability, comparatively easy machining, and weldability. If that were not enough, it is also capable of being anodized, adding a layer of protection for finished
6061 Aluminum is a precipitation-hardened aluminum alloy containing magnesium and silicon as its major alloying elements. It is one of the most versatile of the heat-treatable alloys and offers excellent mability and
Aluminium 6061-T6 mechanical properties are listed in the following tables including yield strength (yield stress), ultimate tensile strength, shear strength, modulus of elasticity, young’s modulus,
General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers offer better chipping characteristics over the T6
6061-T6 aluminum is 6061 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. The graph bars on the material properties cards below compare 6061-T6 aluminum to: 6000-series alloys (top), all aluminum alloys (middle),
Brief introduction to 6xxx wrought aluminum alloys. Tabular data of yield strength, tensile strength, elongation, and modulus of elasticity, at elevated temperatures and at room temperature after heating. Creep, creep
Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and excellent mability, it is perfect for applications in aerospace, transportation equipment and
Applications: Aircraft fittings, camera lens mounts, couplings, marines fittings and hardware, electrical fittings and connectors, decorative or misc. hardware, hinge pins, magneto parts, brake pistons, hydraulic pistons, appliance fittings, valves and valve parts; bike
Aluminum 6061-T6; 6061-T651. General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength, good workability, and high resistance to corrosion; widely
General 6061 characteristics and uses: Notes: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high. strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers. offer better chipping characteristics over the T6
Property 6061-T4 6061-T6 Tensile Strength 241 MPa | 35000 psi 310 MPa | 45000 psi Yield Strength 145 MPa | 21000 psi 276 MPa | 40000 psi Modulus of Elasticity 68.9 GPa | 10000 ksi 68.9 GPa | 10000 ksi Thermal Properties Property 6061-T4 6061-T6 Coefficient of Thermal Expansion 20.0 - 100 °C Temp 23.6 µm/m-°C | 13.1